Ni(OH)2 including 20%Al was synthesized by solid state reaction. The result of XRD indicated that the sample thus prepared was α Ni(OH)2, and its size and crystalline form were much poorer than those of the sample prepared by solution state reaction. TG and DTA curves showed that α Ni(OH)2 began to decompose at higher temperature than β Ni(OH)2. The electrochemical behaviorsof the sample were studied by cyclic voltammetry and constant current charge discharge experiment. It was found that the sample by solid state reaction hadmore excellent electrode reversibility, higher discharge potential and higher discharge capacity.
Ni(OH)2 including 20%Al was synthesized by solid state reaction. The result of XRD indicated that the sample thus prepared was α Ni(OH)2, and its size and crystalline form were much poorer than those of the sample prepared by solution state reaction. TG and DTA curves showed that α Ni(OH)2 began to decompose at higher temperature than β Ni(OH)2. The electrochemical behaviorsof the sample were studied by cyclic voltammetry and constant current charge discharge experiment. It was found that the sample by solid state reaction hadmore excellent electrode reversibility, higher discharge potential and higher discharge capacity.
出处
《无机化学学报》
SCIE
CAS
CSCD
北大核心
2003年第5期535-538,共4页
Chinese Journal of Inorganic Chemistry
基金
江苏省教委自然科学基金资助项目(No.00KJB150005
01KJB150007)
南京师范大学物理化学重点学科基金资助项目(No.121090B501)。